| Typhical
Characteristics |
| Property |
Test
Method |
Unit
Typical Value |
| Melt
Flow Index (190oC/5.0 kg.) |
ASTM
1238 gm./10 min. |
1.0 |
| Density
23oc |
ASTM
D 1505 GM./cm3 |
0.9555 |
| Tensile
Strength at Yield |
ASTM
dD 638 kg./cm3 |
22.5 |
| Elongation
At Break % |
ASTM
D 638 % |
15 |
| Flexuval
Modulus |
ASTM
D 790 kg./cm |
28.200 |
| Notched
Izod Impact Strength |
ASTM
D 256 kg./cm |
no
break |
| Vicat
Softening Point |
ASTM
D 1525oc |
127 |
|
| Note
: Based on injection moulded 3.2 mm thickness type
one specimen of ASTM D 638 |
| |
| EXTURDER |
 |
| The
raw material that is used to produce the filament
in this extrusion process is HDPE granules. Filament
can be made in variable colors and with minimum
of 80 dinear to maximum of 300 dinear sizes. |
| |
| REELING |
 |
| The
conversion of the filament to hank form is done
in this reeling process. |
| |
| WINDING |
 |
| The
hank form filament is then winded into small bobbins. |
| |
| WARPING |
 |
| Here,
the filament is loaded to the beam for the knitting. |
| |
| KNITTING |
 |
| The
filament is knitted to fabric form by knitting machines.
We are producing fabric 100 mess/sq. inch to 250
mess/sq.inch. Knitting is done by quality High-Tech
Flat Raschel Machines. |
| |
| PACKING |
 |